Structures by: Caer L. G.
Total: 6
LaMnSi2
LaMnSi2
Revue de Chimie Minerale (1986) 23, 162-182
a=4.191(3)Å b=17.68(1)Å c=4.073(3)Å
α=90° β=90° γ=90°
Praseodymium iron silicide (1/1/2)
FePrSi2
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (1990) 41, 7 4700-4712
a=4.103(3)Å b=17.04(3)Å c=4.016(3)Å
α=90° β=90° γ=90°
Neodymium iron silicide (1/1/2)
FeNdSi2
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (1990) 41, 7 4700-4712
a=4.072(1)Å b=16.896(4)Å c=3.996(1)Å
α=90° β=90° γ=90°
Neodymium iron silicide (1/1/2)
FeNdSi2
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (1990) 41, 7 4700-4712
a=4.072(1)Å b=16.896(4)Å c=3.996(1)Å
α=90° β=90° γ=90°
Praseodymium iron silicide (1/1/2)
FePrSi2
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (1990) 41, 7 4700-4712
a=4.103(3)Å b=17.04(3)Å c=4.016(3)Å
α=90° β=90° γ=90°
Neodymium iron silicide (1/1/2)
FeNdSi2
Physical Review, Serie 3. B - Condensed Matter (18,1978-) (1990) 41, 7 4700-4712
a=4.082(3)Å b=16.98(3)Å c=4.004(3)Å
α=90° β=90° γ=90°